Polycarbonate Lathi (Baton)

MOQ : 100 Piece

Business Type Manufacturer, Exporter, Supplier, Retailer, Wholesaler, Trader
Material PC (Polycarbonate).
Length 1 Mt ±lOmm
Diameter 25mm ± 2mm
Click to view more

Preferred Buyer From

Location Worldwide

Product Details

Weight
350Gram ±25Gram
Wall Thickness
4.00mm ± 0.5mm (Uniform Distribution)
Colours
Clear Transparent, Khakhi, Black

Power Chem Plast Ltd is a well-known polycarbonate Lathi manufacturer. In our massive manufacturing unit, there are the latest machinery and equipment for manufacturing a qualitative range of our products. We have considerable production and supplying capacity and use high-quality raw materials sourced from certified and reliable vendors. We have a broad distribution network ready to deliver across the nation.


Quality


We assure convincing quality in our products made using the latest machinery at the most reasonable price. There are only premium quality products as we do regular quality checks under the strict supervision of our trained quality team. They make sure that every product conforms to the standards of the Industry.


Operations


We have a broad client base in India, and our clients appreciate the safe and secure package in which we supply our products. We also ensure timely deliveries of our products as per schedules so that the clients. We are valued for our market-leading price.


Order our Polycarbonate lathi today.



Yes! I am interested


Specification

Physical Properties Value / Unit Standard
Density 1.2g/cc ASTM D792
Water Absorption 0 24Hrs.@73F ASTM D 570
Water Absorption at Saturation 0 Equilibrium,73F ASTM D 570
Shrinkage 0.005-0.007 cm /cm Flow.0.125 inch. ASTM D 955

Specification 02

Mechanical Properties Value / Unit Standard
Hardness, Rockwell M. 70 ASTM D 785
Hardness, Rockwell R. 118 ASTM D 785
Tensile Strength @Break 65.5 Mpa Type 1, 2.0 in/ Min, ASTM D 638
Tensile Strength @Yield 62.1 Mpa Type 1, 2.0 in/ Min, ASTM D 638
Elongation at Break 1.1 Type 1, 2.0 in/ Min, ASTM D 638
Elongation at Yield 0.07 Type 1, 2.0 in/ Min, ASTM D 638
Flexural Modulus 2.34 Gpa 0.05 in/min, 2” span, ASTM D 790
Flexural Yield Strength 93.1 Mpa 0.05 in/min, 2” span, ASTM D 790
Fatigue Strength 6.89 Mpa Fatigue Limit, 2.5 MM Cycles, ASTM D 671
Izod Impact, Unnotched 32 J/cm 73F; ASTM D 4812
Tensile Impact Strength 546 kJ/m2 Type “S” ASTM D 1822
Falling Dart Impact 169J 73F, ASTM D 3029
Taber Abrasion, mg/1000 Cycles 10 CS-17, 1 kg; ASTM D 1044
Izod Impact, Notched 0.08 J/cm 73F; ASTM D 256

Specification 03

Electrical Properties Value / Unit Standard
Volume Resistivity Min 1e+017 ohm- cm ASTM D 257
Dielectric Constant 2.96 1 MHz. ASTM D 150
Dielectric Strength 15 kV/mm In ai, 125 mils, ASTM D 149
Dissipation Factor 0.009/0.01 60Hz, STM D 150/ 1 MHz; ASTM D 150
Comparative Tracking Index 250- 400 V (+/-0.125 inch), PLC Code 2 UL 746A
Hot Wire Ignition, HWI 7 – 15 sec (+/-0.125 inch), PLC Code 4, UL 746A
High Amp. Arc Ignition, HAI 60 – 120 arcs Surface (+/-0.125 inch) PLC Code 1, UL 746 A
High Voltage Arc-Tracking Rate HVTR 25.4–80mm/min (+/-0.125 inch), PLC Code 2; UL 746A

Specification 04

Thermal Properties Value / Unit Standard
CTE linear 68oF 68.4 um/ m-deg. C Flow-40F to 200F; ASTM E 831
Heat Capacity 1.26 J/g. deg. C ASTM C 351
Thermal Conductivity 0.19W/m-K ASTM C 177
Deflection Temperature at 0.46 Mpa (66 psi) 138 deg. C 0.250 inch, unannealed, ASTM D 648
Deflection Temperature at 1.8 Mpa (264 Psi) 132 deg. C 0.250 inch, unannealed, ASTM D 648
Vicat Softening Point 154 deg. C Rate B, ASTM D 1525
UL RTI, Electrical 130 deg. C UL 746B
UL RTI, Mechanical with Impact 130 deg. C UL 746B
UL RTI, Mechanical without impact 130 deg. C UL 746B
Flammability, UL 94 HB 0.029 in.